Hot Dipped Vs Electro Galvanized Roofing Nails

Visage stockbyte getty images when metal goes unprotected the effects can be disastrous.

Hot dipped vs electro galvanized roofing nails.

Electro coated nails are cheaper but the galvanizing is visibly thinner. Clevis hangers that are to be used to support piping are available in hot dipped galvanized finish or electro galvanized. The irregular ingots are solid zinc. Hot dipped galvanized nails not used in a nail gun are usually distinctive.

The thickness of hot dip galvanized zinc layer can achieved more than 50 microns the maximum can reach 100 microns. Fas n tite 3 in 11 gauge electro galvanized roofing nails 5 lbs item 108741. The one being held was electro plated and it s rusting after just 12 years. 3 use the grip rite 11 x 1 1 4 in.

The most durable versions are hot dipped labeled hd because they re coated with molten zinc. Next to it is a new electro plated nail. Hot dipped galvanized by russell bowen galvanization locks out the effects of rust and corrosion. Metabo hpt siding nails 2 inch x 092 inch collated wire coil full round head ring shank hot dipped galvanized 3600 count 13365hhpt 4 7 out of 5 stars 80 43 83 43.

3 degree electro galvanized steel roofing nails 5 lb pack for applying roofing asphalt shingles insulation board and felt to wood substrates. The four gray ones are hot dipped nails some have a distinctive irregular coating of pure zinc. Entire structures like buildings and bridges can collapse without warning. Use the grip rite 11 x 1 1 4 in.

Often they have clumps of zinc on the shaft or the coating of zinc is somewhat uneven on some of the nails. Difference between electro galvanized and hot dip galvanized 1. Galvanized nails all the nails have been galvanized. Building the substructure of a porch is a typical job for galvanized nails.

Use short stubby galvanized nails about 2 65 per box for 8d x 1 to anchor your joist hangers. Thus with a hot dip galvanized surface coating there is approximately 30 percent extra zinc content in each unit compared to the electrogalvanized coating.